High performance ceramic abrasive grits of uniform thickness and methods of producing and using the same

ABSTRACT

A ceramic abrasive grain product of a ceramic material composition, said ceramic abrasive grain product comprising at least fifty percent of abrasive grains having a uniform grain thickness of from 0.002 to 0.016 inches and a length such that the grain is self dressing when oriented such that the thickness of the grain is exposed to a workpiece, abrasive products made therefrom and method for manufacturing and using same.

BACKGROUND OF THE INVENTION

This invention relates to the production of very low packing densityceramic abrasive grits and methods of making the same from various knownabrasive materials such as fused aluminum oxide, co-fused aluminumoxide-zirconium oxide or sintered sol gel aluminum oxide, all of whichmay or may not contain various supplementary oxides.

A usual abrasive particle can simplistically be represented by a doubleended cone, whereby one end of the cone is bonded to the abrasiveproduct base and the other end is contacting the steel workpiece. As thecone wears back from the tip of the cone, the wear flat is increasing intwo directions and thus the wear flat area growth rate increases as asquared function of the wear back.

For use in abrasive applications, the above abrasive materials areproduced in bulk form and are crushed to the desired grit size for usein coated or bonded abrasive products. Aluminum oxide abrasive can bemade by refining bauxite in an arc furnace or by melting a Bayer typealumina in an arc furnace and pouring into large molds for cooling. Thecrude is then crushed into the desired grit size. Co-fused aluminumoxide zirconium oxide abrasive is also are furnaced, but it is pouredinto molds which produce very rapid cooling. Such molds may be steelplates with small spacings (about ¼″) between them or molds whichcontain steel balls, whereby the melt flows into the interstitialspaces. This crude is then also crushed into desired grit sizes. Sol gelalumina is made in a water based system, usually extruded, dried,crushed into the desired grit sizes, calcined and fired into abrasivegrit particles.

In all of the above, crushing of the bulk material results in particleswith a three dimensional shape, whereby the dimensions of the particlesin the three axes of the grain are equivalent or nearly equivalent.Abrasive grits for heavy duty bonded applications are desired to haveequal axes which indicate a “blocky” material and is indicative of amaterial with a high packing density. Abrasive grits for paper and clothapplications are desired to have unequal axes which indicate a “sharp”material and is indicative of a material with a lower packing density.The table below illustrates typical packing densities of various bondedand coated abrasive grits.

TABLE I Packing Density 36 Grit Bonded Coated Abrasives Abrasives g/cm³g/cm³ Fused Aluminum Oxide 1.82-1.92 1.73-1.82 Sintered Sol Gel AluminumOxide 1.82-1.92 1.73-1.82 Co-Fused Aluminum Oxide-Zirconium Oxide2.10-2.22 1.99-2.10

The co-fused aluminum oxide-zirconium oxide particles have similarshapes to the fused aluminum oxide and sintered sol gel particles. Thehigher packing densities result from the higher true specific gravity ofthe alumina-zirconia (4.55) versus 3.94-3.92 for the fused aluminum andsol gel alumina.

Generally, the abrasive grits for coated applications are extractedduring the initial crushing of the crude material when the abrasiveparticles are sharper as indicated by a lower packing density. Theabrasive grits for some bonded applications are generally furtherprocessed by milling or impacting to make the particles more blocky asindicted by a higher packing density. In addition, some bondedapplications do require lower packing density or sharper abrasive grits.

of particular interest are the packing densities of the coated abrasivematerials and that they are only slightly lower than the packingdensities of the bonded abrasive materials. The coated abrasive packingdensities are inherent from crushing a bulk material into abrasivegrits. Lower packing density material than shown on the above Table Ifor coated abrasive applications is desirable but not attainable withthe typical crushing of abrasive grits from bulk crude materials. Lowerpacking density abrasive may be associated with providing a longer lifeabrasive product in coated applications i.e. a higher total metalremoval (cut) until removal rate is unacceptable.

An abrasive disc or belt is discarded when the grinding operatorconsiders that it has become dull, which means the metal removal ratehas decreased to approximately 10-20% of the initial metal removal rate.The metal removal rate is a function of the penetration of the abrasiveparticles into the steel workpiece. The penetration of the particlesinto the steel is further dependent on the pressure the abrasive gritsapply to the steel workpiece. The pressure of the abrasive grits on thesteel workpiece is defined by the force of the abrasive particles on thesteel divided by the wear flat area of the particles. As the wear flatarea of the abrasive particles increases, the abrasive grit pressureapplied to the steel workpiece decreases, the abrasive grit penetrationdecreases and the resulting metal removal rate decreases. When agrinding disc or belt is discarded, the wear flat area is very small,0.002 in.² to 0.004 in.² per square inch of abrasive material, dependingon the type and shape of the steel being ground and the force applied tothe abrasive products.

The wear flat area of an abrasive particle is dependent on the wear(wear back) of the particle during grinding. As the wear back increases,the wear flat area increases. To improve the useful cutting life of acoated abrasive product, it is necessary to slow the abrasive grit wearflat growth rate. This may be accomplished with an abrasive grain moreresistant to wear which results in a slower wear back growth rate and aresulting slower wear flat growth rate. Secondly, the abrasive particleshape can be changed to result in a slower wear flat growth rate as theparticle wears back. Thirdly, the shape and consistency of the abrasiveparticle can be altered so that the abrasive particles with terminalwear flat areas can shed the wear flats and expose a new grindingsurface or that the particle can break off below the grinding interfacethereby also removing the terminal wear flat. This shedding or break-offphenomenon can be called self dressing. The terminal wear flat area isdefined as that area which prevents the abrasive particles fromsignificantly penetrating the steel surface with a particular appliedforce.

Ceramic hollow spheres (ceramic bubbles) have been known for some timeand have many applications, one of which is to lower the density ofabrasive products, especially bonded abrasive products. Such bubbles,e.g. alumina or alumina-zirconia bubbles, added to reduce productdensity generally do not provide sharp edges or corners thatsignificantly improve grinding performance; although, such bubbles maypartially or completely fracture during use of the abrasive productwhich conceivably could have some such effect, albeit minor. Suchceramic bubbles are well known as are their methods of manufacture, e.g.by atomizing fused ceramic material, e.g. fused alumina oralumina-zirconia mix with compressed gas, usually compressed air. Suchproducts are readily available in the industry, e.g. from WashingtonMills as DURALAM® hollow ceramic spheres, from Zircar Corporation asZIRCAR® hollow ceramic spheres or from Treibacher Corporation as ALODUR®hollow ceramic spheres.

Such ceramic bubbles may also be made from other processes such as a solgel processes as described in U.S. Pat. No. 5,077,241.

It has also been known to introduce ceramic filaments or rods intoabrasive products, e.g. as described in U.S. Pat. Nos. 5,194,072;5,372,620; and 5,876,470 with idea that the end portions of suchfilaments or rods would retain a certain sharpness. While this may insome respects have validity, use in actual practice can be difficult.This is because to have the appropriate effect, the rods or filamentshave to be appropriately oriented, i.e. a side on exposure of such a rodor filament to a work piece does not act as a good cutting edge.Further, the ends of such rods or filaments may not actually haveparticularly sharp cutting edges since they might be no thinner than thediameter of the rod or filament itself.

BRIEF SUMMARY OF THE INVENTION

It is an object of the present invention to reduce the wear flat growthrate or shed the terminal wear flats and prolong the useful metalremoval rate (cutting life) of abrasive products, especially coatedabrasive products.

It is a further object of the present invention to provide abrasivegrains that are scooped shaped and able to gouge out portions to beremoved from a workpiece.

It is a further object of the invention to provide abrasive grains inthe form of thin curved sheets that are self sharpening in that theycrack or break off as their edges wear to provide new sharp cutting edgesurfaces.

It is a further object of the invention to provide abrasive grains thatare thin sharp plates having greater strength due to curvature.

It is a further object of the invention to provide abrasive grainshaving a microcrystalline structure that permits cracking off of edgeshaving wear flats to expose a new sharp face.

The present invention employs flakes and/or fibers to reduce the wearflat area growth rate with wear back. A flake with uniform thicknessincreases only in one direction with wearback and thus the wear flatarea growth rate is a linear function of wearback vs. a squared functionfor a usual abrasive particle. A fiber does not increase in eitherdirection with wearback and thus the wear flat area is constant withwearback. The wear flat area of a fiber containing abrasive productincreases only as additional fibers enter the grinding interface level.

The above objects may be attained by using abrasive grains formed bycrushing ceramic bubbles. Such grains are thin plates having a curvaturefollowing the curvature of the original ceramic bubble thus resulting ina “scoop” shape. Such a geometric configuration is stronger than a flatplate of the same thickness thus permitting a very thin abrasive edge tobe useful without premature cracking yet at the same time fracturingwhen a wear flat forms, thus permitting more force to be applied to thegrain while permitting self sharpening.

The invention further includes the abrasive grains themselves as well asabrasive products incorporating them.

Preferably, in accordance with the invention, a ceramic abrasive grainproduct of a ceramic material composition is provided. The ceramicabrasive grain product has an average particle size between about 10 andabout 1500 micrometers, a particle size distribution wherein over 50percent by weight of particles have a particle size within a factor of20 of each other, and a packing density of less than 75 percent of thebulk density of an abrasive grain, having about the same averageparticle size and particle size distribution of essentially the sameceramic material composition as the ceramic grain product of theinvention, that was fused, cooled to a solid mass, and crushed to grainsizes. Essentially all (greater than 90%) of the grains of the inventionhave a grain thickness less than twenty percent of the particle size.

In another preferred embodiment of the invention, there is provided anabrasive grain material comprising particles having an internal concavesurface, an external convex surface and a relatively uniform thicknessbetween the internal and external surfaces, the external surface beingof a relatively uniform curvature, which curvature, if extended, wouldform a contiguous surface essentially spherical in shape. The averageparticle size of the grain of the invention is between about 10 andabout 1500 micrometers. The particles have irregular circumferentialedges defined by circumferences of the internal and external surfaces.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIG. 1 shows an abrasive product coated with grains of the presentinvention;

FIG. 2 shows a photomicrograph of an embodiment of abrasive grains ofthe invention made by crushing hollow alumina beads, i.e. “bubbles”;

FIG. 3 shows a magnified view of an abrasive grain of the presentinvention indicating its curvature and sharp edges;

FIG. 4 shows an SEM photomicrograph of grains of the invention at 20×magnification;

FIG. 5 shows an SEM photomicrograph at 800× showing microcrystallinestructure of a grain of the invention wherein microcrystal interfacesare clearly visible that may break to expose a sharper edge; and

FIG. 6 shows an SEM photomicrograph at 2000× of a grain of theinvention.

DETAILED DESCRIPTION OF THE INVENTION

“Particle size” is the median dimension of the particle. “Averageparticle size” of the grains of the invention is defined by the averageof median dimensions of the particles. The “median dimension” is theintermediately sized dimension of the three dimensions of the particle.The median dimension is determined by determining each of x, y, and zmutually perpendicular dimensions through the geometric center of theparticle, where the sum of x, y and z is maximized, and taking thedimension that is intermediate in length between the lengths of theother two dimensions, as the median dimension. “Thickness” of the grainis the smallest of the x, y and z dimensions through the center of thegrain. “Length” of the particle is longest of the x, y and z dimensions.

In general, a method for making the product of the invention includesthe steps of:

-   -   a. forming ceramic bubbles having a diameter of between 20 and        3000 micrometers; and    -   b. crushing the ceramic bubbles to form the product.

From about 0.3 to about 0.7 weight percent of water insoluble ceramicmaterial may be added that melts at a temperature lower than alumina toreduce bubble wall thickness. The lower melting ceramic material may beselected from silicon dioxide, magnesium orthosilicate, and aluminumsilicate. The preferred lower melting ceramic material is silicondioxide.

Additionally, from about 0.1 to about 0.7 weight percent of oxides otherthan alumina and zirconia can be added to cause weakened grainboundaries to improve automatic grain sharpening.

The oxide for this purpose may, for example, be silica or magnesia.

The ceramic bubbles may be formed by a number of methods. For example,fused ceramic material may be atomized with compressed gas or sol gelceramic bubbles formed from blown sol gel followed by sintering.

Materials that can be used to make ceramic bubbles that can be crushedin accordance with the invention include, but are not limited to:alumina, zirconia and silica and mixtures thereof including additivessuch as titania, and rare earth metal oxides.

Crushed Alumina Bubbles with or without additives

Crushed Alumina-Zirconia Bubbles with or without additives

Crushed Silica Bubbles with or without additives.

Crushed Alumina-Titania Bubbles.

The ceramic material of the abrasive product may be selected from fusedand solidified white alumina, fused and solidified brown alumina, fusedand solidified alumina-zirconia ceramic alloy, fused and solidifiedalumina-titania ceramic alloy, and solidified and sintered alumina solgel.

The packing density of abrasive grains is due to a number of variablesincluding density of the material of the grain, average grain size,grain size distribution and grain shape.

The packing density of the abrasive product of the invention, due tograins in the form of thin sheets having curved surfaces, is less thanprior art solid abrasives having the same ceramic type composition andgrain size. This same unique thin wall curved surface is believed to beresponsible for the superior cutting ability of the grains of theinvention providing strong grains with thin sharp cutting edges. Aphotomicrograph of an abrasive grain of the invention can be seen inFIG. 2 at a magnification of about 30×. FIG. 3 shows a drawing of anabrasive particle 16 of the invention showing a thickness 20, a curvedsurface 22 and a sharp edge 24.

As examples, abrasive product consisting essentially of crushed white orbrown alumina bubbles of a diameter of up to about 3000 micrometerscrushed to average particle size (as discussed above) of about 500 to550 micrometers (36 grit) with about a 0.05 mm (0.002 inch) wallthickness, will have a packing density of from about 0.8 to about 1.5g/cm³ depending on wall thickness of the starting bubble. That wallthickness determines the thickness of the grain, which is usually about.0.05 to about 0.4 mm (0.002 to about 0.016 inch). Typical packingdensities for 36 grit alumina grain of the invention is less than 1.5g/cm³ (over about 3,000 particles per gram), preferably less than 1.3g/cm³ (over about 4,000 particles per gram) and for most applications,most preferably less than 1.1 g/cm³ (over about 5,000 particles pergram). For alumina-zirconia grain made from bubbles in accordance withthe invention, due to higher material density, typical packing densitiesfor 36 grit grain is less than 1.7 g/cm³ (over about 2,500 particles pergram), preferably less than 1.5 g/cm³ (over about 3,000 particles pergram) and for most applications, most preferably less than 1.3 g/cm³(over about 3,500 particles per gram)

The grain of the invention is particularly suited for coated abrasiveapplications, e.g. sand paper, but is also well suited for bondedabrasive applications, e.g. grinding wheels, and for free cuttingabrasive applications, e.g. sandblasting.

Coated product 10 of the invention, as for example seen in FIG. 1, has abase sheet 12 of a fiber disc, or fabric, e.g. a woven material orflexible polymer sheet. At least one bonding layer 14, e.g. a resinlayer, is on the surface of the base layer that partially embeds theabrasive grain particles 16 to hold them to the base layer. The bondinglayer may be a ceramic matrix, a resin matrix or mixtures thereof. Thebonding layer is usually a resin, e.g. a phenolic resin.

Bonded abrasive products of the invention are similar to a coatedproduct, as shown in FIG. 1, except that the bonding material is usuallynot flexible and grains may be entirely embedded. In such a product, theflexible base layer is absent; although, reinforcing material or fabricmay be embedded in the bonding layer. 13. The bonding material isusually a bonding matrix selected from the group consisting of a ceramicmatrix, a resin matrix and mixtures thereof.

The invention also includes a method for abrading an article bygrinding, sanding or blasting the article with an abrasive materialusing a material that includes the ceramic abrasive product of theinvention.

EXAMPLES

The grinding results described below were generated with 7″ fiber discstrimmed from 8″ discs coated via conventional techniques with 36 gritmaterials and using KBF₄ in the size coat. The discs were mounted to ahorizontal turntable and rotated at 2500 rpm. Stainless steel (316) bars( 3/16″×1″×24″) were positioned vertically in a holder above the discwith the 1″ direction of the steel bar facing across the disc, in linewith the central axis. The resulting wear track on the disc had anoutside diameter of 6.5 inches and an inside diameter of 4.5 inches. Anauxiliary weight of 8.17 lbs. was set on a holder attached to the bar. Anew bar, the auxiliary weight and the holder for the auxiliary weightattached to the bar was 9.71 lbs., which applied a pressure of 51.8 psifrom the steel bar to the grinding disc. A total of 12 bars with theirauxiliary weight holders were used for sequential grinding for 20 secondintervals. The weight loss for each set of six bars was recorded as theweight loss during a two minute period. As the bars lost weight, anequivalent weight was added to the auxiliary weight to keep the pressureapplied to the disc constant.

Table II shows the cut in grams of two 36 grit (average particle size500 to 550 microns) NZ+1585 grains made into discs which is for use incoated applications. This grain was used for a control. Also shown is anNZ+ comparable abrasive grain, ATZ-II. This second grain was separatedon a diamond shape table into various shape fractions to evaluate theeffect of packing density (i.e. shape or sharpness) on the cut of 316stainless steel.

TABLE II WEIGHT LOSS (CUT) OF 316SS BARS NZ+ NZ+ ATZ-II Shape Table NANA 1-5 9 10 11 12 Compartments Packing Density g/cm³ 2.01 2.01 2.16 2.072.00 1.93 1.82 Time (Minutes)  2 25.6 23.9 16.1 22.8 28.6 32.8 35.0  413.8 13.4 9.8 14.4 14.8 19.6 22.7  6 12.4 8.2 6.5 10.7 11.5 15.6 17.7  88.6 6.9 6.0 7.8 8.9 12.0 13.3 10 6.8 5.3 5.7 6.5 6.8 9.3 11.6 12 5.3 4.65.1 5.1 5.2 7.8 9.7 Total Cut (grams) 72.5 62.3 49.2 67.3 75.8 97.1110.0 Dist Wt. Loss (grams) 1.51 1.38 .90 1.18 1.40 1.73 1.86 TestNumber 503 507 417 418 419 420 421

Table II illustrates the importance of using a low packing density(sharp) commercial abrasive material to obtain higher cuts. The packingdensities are illustrative of lowest available packing densities for“sharp” grains of the prior art but are not nearly as low as packingdensities of grains of the present invention. The discs weight losscorrelates very well with the packing densities and cuts. The blockiergrains (high packing density) have a shape which results in a largerwear flat area for a specific wear back compared to sharper elongatedgrains which would have a smaller wear flat area for the same wear back.Thus, the blocky material, which has a higher wear flat area growthrate, also has a more rapidly declining cutting rate and a lower totalcut. The smaller wear back for the blocky grains results in a lower discweight loss. The sharper grains cut more aggressively, have a greaterwear back and probably also have wear flat grains breaking off whichcontribute to a higher disc weight loss.

A description of the physical properties of alumina bubbles is necessaryto explain the results on Table III and IIIA.

The shell thickness of alumina bubbles varies with the SiO₂ content andthe bubble size. Generally, bubbles blown from Al₂0₃ fusions containing0.3 to 0.7% SiO₂ have the thinnest wall thickness. As the SiO₂ leveldecreases or increases from that level, the wall thickness graduallyincreases. In addition, wall thickness decreases with decreasing bubblesize as illustrated on the following Table IIA. As the bubble sizedecreases, the wall thickness decreases which results in a decreasing 36grit packing density and an increasing number of particles per gram andfewer particles on the abrasive disc shown in Tables III and IIIA. TableIIA is for illustration only. The material is not the same materiallisted on Table III and IIIA.

TABLE IIA 36 GRIT (500 to 550 micrometers) FROM CRUSHED BUBBLES MeshBubble Size +5 9/5 14/9 18/14 (>4 mm) (2-4 mm) (1-2 mm) (0.8-1 mm) .49%SiO₂ wall thickness - inches .008-.015 .004-.008 .002-.004 Not particlesper gram 4096 5154 6639 Processed 36 grit packing density 1.20 1.10 0.89.34% SiO₂ wall thickness .008-.015 .004-.008 .002-.004 .002 or lessparticles per gram 4135 4956 6443 8155 36 grit packing density 1.18 1.07.89 .73 0% SiO₂ wall thickness * * .002-.006 .002-.004 particles pergram 6055 6427 36 grit packing density 1.05 .97 * This size bubbles notavailable.Table III shows the cut in grams for 36 grit NZ+ 1585, which was used asa control. Also shown are 36 and 30 grit materials made from crushed4/10 and 10/14 alumina bubbles. Also shown is a 36 grit material madefrom crushed 6/14 NZ+ comparable bubbles. The grinding test for eachindividual grain was terminated when the cut reached approximately 5grams in a two minute period.

TABLE III WEIGHT LOSS (CUT) OF 316SS BARS FOR VARIOUS BUBBLE MATERIALS36 30 36 30 36ATZ-II 36NZ+ 4/10 4/10 10/14 10/14 6/14 % SiO₂ .49 .49 .28.28 Grams of Size on 8″ Disc 32.0 32.0 39.0 33.0 37.0 33.0 Grams ofGrain on 7″ Disc 22.4 13.4 13.5 10.6 10.7 20.8 Packing Density g/cm³2.01 1.01 .95 .86 .81 1.37 NZ+ & ATZ-II Packing Density* 1.59 1.15Particles Per Gram 2028 4805 — 5712 — 3432 NZ+ & ATZ-II Part. Per Gram*2563 4098 Time (Minutes)  2 25.6 14.8 12.4 10.5 11.2 22.6  4 13.8 14.213.0 11.2 13.5 17.3  6 12.4 13.4 12.2 12.1 13.2 12.7  8 8.6 11.7 10.611.3 12.3 11.0 10 6.8 9.7 10.0 10.7 11.9 9.7 12 5.3 8.9 9.2 9.9 11.1 8.914 8.0 8.8 9.9 10.4 7.9 16 7.2 8.2 9.6 10.1 7.7 18 6.3 7.7 9.1 9.8 7.520 5.7 7.1 8.9 9.3 6.5 22 6.9 8.4 8.7 6.3 24 6.3 8.3 8.4 5.8 26 6.1 8.17.9 28 5.6 8.1 7.9 30 5.5 7.8 7.2 32 7.5 6.9 34 7.3 6.6 36 7.1 6.4 387.0 5.9 40 6.7 5.6 42 6.5 44 6.3 46 6.2 48 5.7 Total Cut 72.5 99.9 129.6204.2 184.3 129.4 Disc Wt. Loss 1.51 3.12 3.73 5.87 5.86 2.91 Test No.503 562 558 565 564 568 36 4/10: 36 grit produced by crushing 4/10alumina bubbles 30 4/10: 30 grit produced by crushing 4/10 aluminabubbles 36 10/14: 36 grit produced by crushing 10/14 alumina bubbles 3010/14: 30 grit produced by crushing 10/14 alumina bubbles 36 ATZ-II: 36grit produced by crushing 6/14 alumina-zirconia bubbles *NZ+ and ATZ-IIpacking density and particles per gram adjusted to a specific gravity of3.60, the same specific gravity of the alumina bubbles.

The grain crushed from bubbles (flakes) had a significantly higher cutthan the NZ+ control, cut for a longer time and had a higher weightloss. While not wishing to be bound by any particular theory, thisphenomenon is believed to result from the following:

First, it is believed that the flake shape particles have a slower wearflat growth rate with wear back as noted previously, and therefore grindfor a longer time before reaching the terminal wear flat area when thegrinding product is discarded.

Second, it is believed that because of the weaker shape, the wear flatsmay shed (ablate) as they increase in size and receive more frictionforce from the grinding operation, and

Third, it is believed that because of the weaker shape, the grains withwear flats may break off below the grinding surface and thus allow newgrains to engage the steel surface.

Shedding or ablation and breakoff can be considered self dressing, andthis concept is supported by the higher disc weight loss compared withNZ+. In all test results the higher cuts always correlate with higherdisc weight loss.

The grain made from the 10/14 alumina bubbles had higher cuts than thegrain made from 4/10 alumina bubbles. The grain made from the 10/14bubbles had a lower packing density, thinner walls and a larger numberof particles per gram, all of which improved the cut. The grain madefrom the alumina-zirconia bubbles had a higher packing density, athicker shell wall 0.005″-0.010″ and fewer particles per gram. Thinnerwall bubbles should achieve a higher cut. The alumina-zirconia is alsobelieved to be a tougher material and may not break back as readily asthe grain made from alumina bubbles. The lower weight loss of the ATZ-IIsample on Table III (2.91 g) supports this concept.

Another important aspect of grain from crushed bubbles is that the steelsurface finish is finer. The cutting edge of a grain produced fromcrushed bubbles is composed of micro crystals as asperites and resultsin a finer surface finish compared with a large single grain cuttingpoint as in NZ+. The finer surface finish of steel using crushed bubblesallows coarser gradings to be used in the manufacture of belts anddiscs, i.e. 30 grit crushed alumina bubbles to replace 40 or possibly 50grit NZ+. The surface roughness of the steel bars ground with 36 NZ+ and30 10/14 was 2783 micro-inches and 1577 micro-inches respectively after2 minutes of grinding and 1836 micro-inches and 730 micro-inches after12 minutes of grinding.

From Table III, the improved performance of crushed alumina bubbles vs.NZ+ can be calculated.

${\frac{36\mspace{14mu} {4/10}\mspace{14mu} {Alo}\mspace{14mu} {Cut}\mspace{14mu} 99.9\mspace{14mu} g}{{NZ} + {{Cut}\mspace{14mu} 72.5\mspace{14mu} g}} \times \frac{{22.4\mspace{14mu} g\mspace{14mu} {of}\mspace{14mu} {NZ}} + {{on}\mspace{14mu} {Disc}}}{13.4\mspace{14mu} g\mspace{14mu} {of}\mspace{14mu} {Grain}\mspace{14mu} {on}\mspace{14mu} {Disc}}} = 2.30$

That is, 36 grit from 4/10 crushed alumina bubbles has a performance230% higher than NZ+.

Using the same procedure: Performance % Grain Above 36 NZ+ 36 gritcrushed 4/10 alumina 230 30 grit crushed 4/10 alumina 297 36 gritcrashed 10/14 alumina 595 30 grit crushed 10/14 alumina 548 36 gritcrushed 6/14 alumina-zirconia 192

Again, while not wishing to be bound by any particular theory, it isbelieved that the difference in the cut and disc weight loss phenomenonbetween NZ+ and the crushed bubble materials can be explained by wearflat areas. The NZ+ initially has sharper points, and therefore asmaller initial wear flat area and a higher cut. But the blockier NZ+material has a more rapid wear flat area growth rate during wear back.In comparison, the flakes from the crushed alumina bubbles have aninitial higher wear flat area, but the wear flat area growth rate isslower during wear back and/or self dressing occurs to reduce the wearflat growth rate.

Another test was designed to determine if the amount of size has aneffect on cut. In previous test coating runs (before Table III) toevaluate various abrasives, 28-30 grams of size was always applied tothe 8″ fiber discs in two coatings, based on data in a 3M U.S. Pat. No.4,770,671. Because of the assumed fragile nature of the crushed aluminabubble shells, it was decided to increase the amount of size on thediscs in Table III to provide improved or additional support.

Table IIIA includes the same lot of 10/14 material (0.28% SiO₂) as inTable III with various weights of size. Included are two NZ+ discs with21 and 28 g of size. The results indicate that for crushed bubbles thereis an optimum amount of size which gives optimum performance. The NZ+results indicate that 21, 28 or 32 g (Table III) of size has no effecton cut.

A second set of grains on Table IIIA are labeled 0% SiO₂. The 25 and 28g of size on the 0% SiO₂ grains had a higher cut than the 25 and 28 g ofsize on the 0.28% SiO₂ samples. This was unexpected because the 0% SiO₂material has a higher packing density, fewer particles per gram andslightly thicker shell walls. One explanation is that the absence ofSiO₂ improves total cut.

TABLE IIIA WEIGHT LOSS (CUT) OF 316SS BARS FOR VARIOUS MATERIALS 36 3636 36 36 36 36 36 36 NZ+ NZ+ 10/14 10/14 10/14 10/14 10/14 10/14 10/14 %SiO₂ .28 .28 .28 .28 0 0 0 Grams size on 8″ disc 28 21 21 25 28 31 23 2528 Grams grain per 7″ disc 23.4 24.1 10.2 10.3 10.3 10.6 12.4 13.1 12.5Packing density g/cm³ 2.01 2.01 .86 .86 .86 .86 1.05 1.05 1.05 Particlesper gram 2028 2028 5712 5712 5712 5712 4910 4910 4910 Time (Minutes)  226.2 30.5 26.1 25.0 20.8 18.2 26.4 23.6 19.8  4 16.8 16.8 17.5 18.7 16.015.6 19.6 20.3 18.2  6 12.1 11.1 13.3 14.9 13.1 13.7 16.3 17.3 16.1  87.9 8.5 11.1 12.5 12.0 12.8 13.4 14.5 14.3 10 6.4 6.2 9.9 10.8 10.3 11.311.7 12.4 13.2 12 4.7 5.0 9.2 9.8 9.0 10.2 9.5 11.1 11.8 14 8.5 8.8 8.49.6 8.6 10.0 11.0 16 7.6 7.8 7.7 8.8 7.2 9.2 9.9 18 6.2 6.3 7.2 8.2 6.68.0 9.2 20 5.4 5.5 6.3 7.8 6.0 7.2 8.6 22 4.7 5.0 6.0 7.1 5.3 6.4 8.0 245.9 6.7 5.8 7.3 26 5.5 6.2 5.5 6.5 28 5.3 5.9 5.2 6.2 30 4.9 5.8 5.9 325.4 5.3 34 5.2 Total Cut (g) 74.1 78.1 119.5 125.1 138.4 158.5 130.6146.5 171.3 Disc Wt. Loss (g) 1.46 1.68 3.55 3.57 3.87 4.36 3.75 4.034.71 Test No. 589 593 594 595 603 599 588 602 587 Performance % 100 —370 384 424 472 333 353 433

The same concepts that were discussed for the fused alumina and fusedalumina zirconia materials are applicable with respect to alumina solgel here and will not be discussed again. Data will be presented whichconcurs and supports the concepts of the previous section.

In the first case, ribbons of composition 321 were extruded into variousthicknesses, dried, crushed 18 gg×26 gg; calcined at 650° C., fired at1370° C. for 6 minutes and graded into 36 grit.

The approximately extruded and fired thickness is shown below:

Extruded Thickness: .099″ .058 .036 .027 .020 Fired Thickness: .015″.010 .0065 .005 .004

The various samples were made into coated discs via the same process asdiscussed previously and tested by grinding 316 stainless steel bars asdiscussed previously. The results are shown in Table IV. Included in theresults are controls of a 3M commercial disc (985C) and 3M commercialgrain (321) made into discs at the same time the ribbon discs were made.

The grinding test was terminated when the metal removal rate for a twominute interval decreased below 11 grams.

TABLE IV WEIGHT LOSS (CUT) OF 316SS BARS VIA 36 GRIT DISCS MADE WITHCRUSHED RIBBONS 3M 3M WM** 985C 321 321 Extruded Thickness — — — .099.058 .036 .027 .020 Fired Thickness — — — .015 .010 .0065 .005 .004Grams on Grain on Disc  19* 19 19 19 19 19 18 17 Packing Density g/cm³ —1.81 1.63 1.70 1.72 1.59 1.43 1.33 Particles Per Gram NA 2726 3050 28742842 3212 4000 4351 Time (Minutes)  2  54.2 40.2 54.7 31.2 40.0 45.540.1 43.5  4  20.1 26.0 36.8 22.8 29.4 30.6 33.6 32.2  6  12.3 22.7 24.520.2 25.2 27.0 29.2 27.3  8  8.7 16.4 19.0 19.9 23.6 24.9 24.9 26.5 10 8.1 12.2 13.2 16.5 18.4 23.1 20.9 23.3 12  7.8 9.4 11.2 17.1 16.0 18.219.1 20.9 14 10.0 12.5 13.2 15.6 17.7 18.4 16 12.2 11.4 12.4 14.7 15.818 10.4 9.7 10.5 12.8 15.0 20 10.5 13.2 22 11.6 24 g. Total Cut 111.2126.9 169.4 162.8 186.9 207.8 224.1 247.7 g. Disc Wt. Loss  1.64 2.252.68 2.84 2.79 3.45 4.37 4.82 Test No. 404 521 393 500 502 512 519 528Performance % 100 133 128 147 164 197 247 *Approximately 30% of thegrain on this disc was 40 grit fused brown aluminum oxide **A 3M 321equivalent composition made by Washington Mills Electro Minerals

The 985 C commercial disc had a high initial cut which is typical of asharper grain. However, the 985C disc had a very rapid cut decay and avery low weight loss which is typical of blocky grain. The packingdensity of the sol gel grain on this disc could not be determinedbecause it was mixed with approximately 30% brown aluminum oxide.

The commercial 3M 321 grain was used as a control for the remaininggrains in the series. The grain labeled WM 321 was an equivalentcomposition similar to the 3M 321 but was much sharper and crushed fromthe crude material via a special technique. This sharper grain resultedin a higher cut and also a higher disc weight loss.

As the extrusion thickness of the ribbon grain decreased, the packingdensity decreased the particles per gram increased, the cut increasedand the disc weight loss increased. Thus when an abrasive disc or beltis made from 0.020″ extruded material, the cut will be much higher and20-30% of the abrasive will be consumed compared to 10-20% for discs orbelts made with conventional abrasives.

The product made with the extruded ribbons had improved cut relative tocommercial alumina abrasive products but the performance factor of theextruded ribbons was not nearly as good as the performance factor of thelow bulk density ceramic bubble grain of the invention previouslydescribed.

In a further test, fine rods were extruded via a die with multiple holesof 0.031″. The dried material was partially crushed, calcined at 650°C., then further crushed by hand rubbing on a 14 mesh round 8″ U.S.standard screen. Below this 14 mesh screen was a screen stack, 20, 25,30, 35, 40, 45, 50 Pan. The rods were then screen categorized and firedat 1370° C. for six minutes. The rod diameter was approximately 0.007″.

U.S. Screens Average Length 25-30 .080-.090 30-35 .060-.070 35-40.060-.070 40-45 .050-.060 45-50 .030-.040 Pan

The rods were used as the above fractions and were not graded into 36grit. The grinding results are shown on Table V. Some discs were madewith combinations of rods and ribbons and rods and 321 μM.

TABLE V WEIGHT LOSS (CUT) OF 316SS BARS VIA DISCS MADE WITH RODS OR RODSAND RIBBONS Rod Size U.S. Sieves 3M 321 45-50 40-45 30-40 25-30 Grams ofRods  19* 10.7 20.3 7.9 7.7 11.5 17.1 Grams of .020″ Ribbons 9.1 Gramsof WM 321 9.3 12.8 8.6 Packing Density of Rods  1.81* 1.54 1.54 1.491.47 Time (Minutes)  2  40.2 29.6 17.0 36.1 27.1 31.9 24.0  4  26.0 26.619.9 33.0 24.9 29.0 21.3  6  22.7 23.6 20.4 27.2 20.6 26.9 18.6  8  16.421.8 18.8 23.7 19.6 24.4 17.4 10  12.2 20.4 19.0 23.5 17.8 21.5 14.6 12 9.4 18.6 15.8 23.2 17.0 21.3 12.9 14 18.1 16.0 21.6 16.7 19.2 12.9 1615.0 14.7 18.9 15.9 18.0 13.7 18 14.0 13.8 17.1 15.7 17.6 13.8 20 12.113.5 16.0 15.1 16.1 12.9 22 11.5 12.3 14.3 14.0 16.5 11.1 24 9.8 11.212.2 13.9 16.0 11.0 26 10.5 10.8 13.4 15.5 10.6 28 13.4 14.1 30 13.613.7 32 13.0 13.4 34 13.2 12.0 36 11.8 11.2 38 10.9 10.7 Total Cut 126.9221.0 202.9 277.6 307.7 348.0 209.5 Disc Wt. Loss  2.25 4.21 4.98 5.865.95 7.56 5.08 Test No. 521 548 549 550 554 555 575 Performance % 100165 150 244 225 259 183 Performance calculated via cut and grams ofgrain on disc. *grams and packing density of grain - not rods

In all cases, the cuts and disc weight losses were higher to much higherthan the 3M 321 control. Again, this cut was superior but still not asgood as the crushed alumina bubbles as previously described. Thebelieved explanation is as before, slower wear flat growth rate and selfdressing, both of which contribute to a longer life and higher cut.

Mixtures of rods and ribbons or rods and WM 321 had higher cuts thanrods alone and also had the highest disc weight loss. This could be theresult of ribbons and WM 321 providing support for the rods duringgrinding. There also may be a synergistic effect which promotes selfdressing.

The discs in this series had extra size material which may havecontributed a small amount to the higher disc weight loss.

What is claimed is:
 1. A ceramic abrasive grain product of a ceramicmaterial composition, said ceramic abrasive grain product comprising atleast fifty percent of abrasive grains having a uniform grain thicknessof from 0.002 to 0.016 inches and a length such that the grain is selfdressing when oriented such that the thickness of the grain is exposedto a workpiece.
 2. The ceramic abrasive grain product of claim 1,wherein the abrasive grains are crushed, extruded and fired sol gel. 3.The ceramic abrasive grain product of claim 2 1 wherein the abrasivegrains are crushed extruded and fired sol gel ribbons.
 4. The ceramicabrasive grain product of claim 1 comprising crushed ceramic bubblesformed from blown and sintered sol gel ceramic material.
 5. The ceramicabrasive grain product of claim 1 wherein the abrasive grains arecrushed extruded and fired sol gel filaments or rods.
 6. The ceramicabrasive grain product of claim 1 wherein the ceramic material of theabrasive product is selected from the group consisting of fused andsolidified white alumina, fused and solidified brown alumina, fused andsolidified alumina-zirconia ceramic alloy, fused and solidifiedalumina-titania ceramic alloy, and solidified and sintered alumina solgel.
 7. A coated abrasive product comprising a sheet material havingceramic abrasive grain product of claim 1 partially embedded in a resinlayer on a base layer.
 8. A coated abrasive product comprising a sheetmaterial having ceramic abrasive grain product of claim 2 partiallyembedded in a resin layer on a base layer.
 9. A coated abrasive productcomprising a sheet material having ceramic abrasive grain product ofclaim 3 partially embedded in a resin layer on a base layer.
 10. Acoated abrasive product comprising a sheet material having ceramicabrasive grain product of claim 4 partially embedded in a resin layer ona base layer.
 11. A coated abrasive product comprising a sheet materialhaving ceramic abrasive grain product of claim 5 partially embedded in aresin layer on a base layer.
 12. A coated abrasive product comprising asheet material having ceramic abrasive grain product of claim 6partially embedded in a resin layer on a base layer.
 13. A bondedabrasive product comprising the ceramic abrasive material of claim 1embedded in a bonding matrix selected from the group consisting of aceramic matrix, a resin matrix and mixtures thereof. 14-30. (canceled)31. A method for manufacturing the product of claim 1 comprising: a.extruding a sol gel in the form of a filament, rod or ribbon having auniform thickness permitting firing to a uniform thickness of from 0.002to 0.016 inches; and b. firing to a uniform thickness of from 0.002 to0.016 inches; and c. crushing the fired filament, rod or ribbon to formthe product. 32-36. (canceled)
 37. A method for abrading an articlecomprising grinding, sanding or blasting the article with an abrasivematerial comprising the ceramic abrasive product of claim
 1. 38. Amethod for abrading an article comprising grinding, sanding or blastingthe article with an abrasive material comprising the ceramic abrasiveproduct of claim
 7. 39. A method for abrading an article comprisinggrinding, sanding or blasting the article with an abrasive materialcomprising the ceramic abrasive product of claim
 13. 40. The ceramicabrasive grain product of claim 1 comprising crushed ceramic bubblesblown from an alumina fusion containing from 0.3 to 0.7 percent of SiO₂.